From: Low temperature method for the production of calcium phosphate fillers
M100% | HAp30%+M70% | HAp50%+M50% | HAp60%+M40% | HAp70%+M30% | HAp80%+M20% | HAp90%+M10% | |
---|---|---|---|---|---|---|---|
HAp 100% | p < 0.01 | p < 0.005 | p < 0.0005 | n.s. | p < 0.005 | p < 0.0005 | p < 0.005 |
HAp90%+M10% | n.s. | p < 0.0005 | p < 0.0005 | p < 0.005 | n.s. | p < 0.0005 | |
HAp80%+M20% | p < 0.0005 | p < 0.0005 | p < 0.1 | p < 0.0005 | p < 0.0005 | ||
HAp70%+M30% | n.s. | p < 0.0005 | p < 0.0005 | p < 0.0005 | |||
HAp60%+M40% | p < 0.005 | p < 0.0005 | p < 0.0005 | ||||
HAp50%+M50% | p < 0.0005 | p < 0.0005 | |||||
HAp30%+M70% | p < 0.0005 | ||||||
M100% | HAp30%+M70% | HAp50%+M50% | HAp60%+M40% | HAp70%+M30% | HAp80%+M20% | HAp90%+M10% | |
HAp 100% | p < 0.005 | p < 0.0005 | p < 0.0005 | n.s. | p < 0.0005 | p < 0.0005 | p < 0.0005 |
HAp90%+M10% | p < 0.0005 | n.s. | p < 0.0005 | p < 0.0005 | n.s. | p < 0.0005 | |
HAp80%+M20% | p < 0.0005 | p < 0.0005 | p < 0.025 | p < 0.0005 | p < 0.0005 | ||
HAp70%+M30% | p < 0.0005 | p < 0.025 | p < 0.0005 | p < 0.0005 | |||
HAp60%+M40% | p < 0.005 | p < 0.0005 | p < 0.0005 | ||||
HAp50%+M50% | p < 0.0005 | p < 0.0005 | |||||
HAp30%+M70% | p < 0.0005 | ||||||
M100% | HAp30%+M70% | HAp50%+M50% | HAp60%+M40% | HAp70%+M30% | HAp80%+M20% | HAp90%+M10% | |
HAp 100% | n.s. | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 |
HAp90%+M10% | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.1 | P < 0.05 | p < 0.0005 | |
HAp80%+M20% | p < 0.0005 | p < 0.0005 | p < 0.005 | p < 0.0005 | p < 0.0005 | ||
HAp70%+M30% | p < 0.0005 | p < 0.005 | p < 0.0005 | p < 0.005 | |||
HAp60%+M40% | p < 0.0005 | p < 0.0005 | p < 0.0005 | ||||
HAp50%+M50% | p < 0.0005 | p < 0.0005 | |||||
HAp30%+M70% | p < 0.0005 | ||||||
M100% | HAp30%+M70% | HAp50%+M50% | HAp60%+M40% | HAp70%+M30% | HAp80%+M20% | HAp90%+M10% | |
HAp 100% | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 |
HAp90%+M10% | n.s. | p < 0.1 | p < 0.0005 | p < 0.025 | n.s. | p < 0.0005 | |
HAp80%+M20% | p < 0.0005 | p < 0.0005 | p < 0.01 | p < 0.0005 | p < 0.0005 | ||
HAp70%+M30% | n.s. | p < 0.0005 | p < 0.0005 | p < 0.005 | |||
HAp60%+M40% | p < 0.025 | p < 0.0005 | p < 0.0005 | ||||
HAp50%+M50% | p < 0.0005 | p < 0.05 | |||||
HAp30%+M70% | p < 0.0005 | ||||||
M100% | HAp30%+M70% | HAp50%+M50% | HAp60%+M40% | HAp70%+M30% | HAp80%+M20% | HAp90%+M10% | |
HAp 100% | n.s. | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 | p < 0.0005 |
HAp90%+M10% | p < 0.0005 | p < 0.01 | p < 0.0005 | p < 0.025 | p < 0.1 | p < 0.0005 | |
HAp80%+M20% | p < 0.0005 | p < 0.0005 | p < 0.1 | p < 0.0005 | p < 0.0005 | ||
HAp70%+M30% | p < 0.0005 | p < 0.005 | p < 0.0005 | p < 0.0005 | |||
HAp60%+M40% | p < 0.0005 | n.s. | p < 0.0005 | ||||
HAp50%+M50% | p < 0.0005 | p < 0.0005 | |||||
HAp30%+M70% | p < 0.0005 |