Table 3 Median values and IQR of the Young’s Modulus \(E\), yield stress \({\sigma }_{\mathrm{y}}\) and DR of the tensile tests on tube specimens

From: Temperature-dependent tensile properties of polyamide 12 for the use in percutaneous transluminal coronary angioplasty balloon catheters

Temperature [°C] State \({E}_{1\mathrm{mm}/\mathrm{min }}\) [MPa] (IQR) \({E}_{50\mathrm{mm}/\mathrm{min}}\) [MPa] (IQR) \({\sigma }_{y}\) [MPa] (IQR) \(DR\) [%] (IQR)
23 Dry 863.9 (44.9) 908.7 (8.5) 32.3 (0.6) 86.9 (1.3)
  Cond 687.6 (58.9) 844.6 (30.7) 28.6 (2.0) 86.8 (2.8)
37 Dry 733.5 (113.5) 801.1 (19.2) 26.7 (1.5) 83.8 (1.8)
  Cond 567.3 (62.8) 651.9 (20.6) 21.2 (0.8) 90.9 (2.1)
50 Dry 349.9 (64.2) 372.8 (23.6)
80 Dry 190.1 (10.8) 249.5 (19.0) 12.9 (0.5)
100 Dry 131.2 (18.2) 167.9 (34.4) 11.1 (0.9)