Table 2 Median values and IQR of the Young’s Modulus \(E\), yield stress \({\sigma }_{\mathrm{y}}\) and DR of the tensile tests on dog bone specimens

From: Temperature-dependent tensile properties of polyamide 12 for the use in percutaneous transluminal coronary angioplasty balloon catheters

Temp. [°C] State \({E}_{1\mathrm{mm}/\mathrm{min}}\) [MPa] (IQR) \({E}_{50\mathrm{mm}/\mathrm{min}}\) [MPa] (IQR) \({\sigma }_{y}\) [MPa] (IQR) \(DR\) [%] (IQR) \({\nu }_{1\mathrm{mm}/\mathrm{min}}\)
[−] (IQR)
\({\nu }_{50\mathrm{mm}/\mathrm{min}}\)
[−] (IQR)
23 Dry 1506.5 (51.4) 1553.5 (233.1) 45.5 (0.4) 82.8 (0.9) 0.47 (0.06) 0.37 (0.19)
  Cond 728.0 (161.3) 882.0 (341.5) 36.2 (0.4) 90.9 (0.9) 0.36 (0.14) 0.31 (0.11)
37 Dry 869.1 (36.6) 1036.3 (35.0) 34.9 (0.3) 91.9 (0.7) 0.44 (0.03) 0.44 (0.01)
  Cond 533.9 (6.2) 641.5 (5.4) 28.9 (0.2) 97.4 (0.3) 0.42 (0.01) 0.46 (0.01)
50 Dry 514.3 (5.5) 606.2 (11.1) 28.0 (0.4) 98.4 (0.8) 0.40 (0.03) 0.46 (0.01)
  Cond 393.6 (7.9) 446.4 (12.3) 23.8 (0.2) 0.41 (0.03) 0.46 (0.01)
80 Dry 280.0 (10.5) 315.2 (1.2) 18.4 (0.2) 0.35 (0.06) 0.47 (0.01)
  Cond 1263.6 (6.9) 297.6 (3.1) 17.1 (0.2) 0.32 (0.04) 0.47 (0.01)
100 Dry 250.6 (3.2) 272.1 (2.9) 15.5 (0.1) 0.43 (0.04) 0.47 (0.01)
  Cond 243.2 (4.7) 261.1 (3.9) 14.9 (0.1) 0.44 (0.07) 0.47 (0.01)