From: Fabrication and in vitro evaluation of an articular cartilage extracellular matrix-hydroxyapatite bilayered scaffold with low permeability for interface tissue engineering
HAp 35 mg/mL
HAp 70 mg/mL
HAp 105 mg/mL
HAp 140 mg/mL
Peak load (N)
1.33 ± 0.21
0.86 ± 0.06
0.54 ± 0.10
0.28 ± 0.04
Shear stiffness (N/mm)
1.28 ± 0.13
0.79 ± 0.09
0.41 ± 0.05
0.22 ± 0.08